Mainbond® Sun
Mainbond® Sun

Mainbond® Sun

Benefits

Indications

Specifications

Product details
Composition
(content in mass %)
Au 74.0
Ag 14.5
Pt 1.5
Pd 1.5
Zn 1.5
In 1.0
Ta 0.1
Ir 0.1
Type (Classification acc. EN ISO 22674) 4 (s/v/k)
s= self-hardening alloy after slow cooling in the mould
v= Condition after hardening
k= Bonding alloy: condition after ceramik firing
Shade Yellow
Indication Inlays, cervical restorations
MOD Inlays
Crowns
Bridges
Milling technique
Cast posts
Can be veneered with high expansion,
low fusing ceramics
Implant restorations
Article Code 1491 0000
Technical data, melting and casting
Melting range(1) Solidus 950 °C
Liquidus 1030 °C
Preheating Temperature 750 °C
Casting Temperature 1160 °C
Crucible Graphite
Density(1) 15.7 g/cm³
Hardness, HV5 w/k 160/250
v 240(3)
s 235
0.2 % proof strength(1), MPa(2) w/k 700
v 660(3)
Elongation(1) % w/k 4
v 4(3)
Elastic modulus (1), GPa(2) 100
Ceramic firing
CTE 16.3
Oxide firing 800 °C
10 min.
vacuum - no
Soft annealing 650 °C
15 min.
Processing after oxide firing Pickling in Hera AM 99 ca. 70°C / 10 min.
Cooling after ceramic firing
(Relexation cooling is recommended for lang span, bulky frameworks)
HeraSun: Rapid cooling
At the end of the programm the firing platform is completely and firing tray with objects is removed emediately. The firing tray can cool next to the furnace on a fire-resistant tray.
Hardening 500(5)°C
10 min.(5)
Solder / Laser welding wire
Prior to Ceramic Firing
Solder HeraSun Lot 1
HeraSun 900 Lot 1
Working temperature °C: 900 / Solder colour: yellow
After Ceramic Firing
Solder HeraSun Lot 2
Flux** Work. temp.* 710(5)°C / Solder colour: yellow
Alloy also available as Laser welding wire
Ø 0.5 mm x 200 mm +
Ø 0.3 mm x 200 mm +