Bio Ceram Plus® - for C&B
Bio Ceram Plus® - for C&B

Bio Ceram Plus® - for C&B

Benefits

Indications

Specifications

Product details
Composition
(content in mass %)
Au 90.0
Pt 7.9
Zn 1.5
Ir < 0.1 Mass %
Fe 0.1
Mn 0.1
Rh 0.2
Nb 0.1
Ce < 0.1 Mass %
Type 4 (s/ v/ k)
Shade dark yellow
Indication
Crowns
Bridges
Milling technique
Implant restorations (A)
Article Code 1252 0000
Technical data, melting and casting
Melting range(1) Solidus 1040 °C
Liquidus 1100 °C
Preheating temperature 850 °C
Casting temperature 1250 °C
Crucible Graphite
Density(1) 19.0 g/cm³
Hardness (HV5) 220 (w/k), 220³ (v), 180 (s)
0.2 % proof stress(1), MPa(2) 520 (w/k), 520³ (v)
Elongation(1) (%) 3 (w/k), 3 (v)
Elastic modulus(1), GPa (2) 87
Ceramic firing
CTE 14.7
Oxide firing 880°(1) C/ 10 min. (vacuum)
Soft annealing ---
Processing after oxide firing Pickling in Hera AM 99 ca. 70°C / 10 min.
Cooling after ceramic firing
(Relexation cooling is recommended for lang span, bulky frameworks)
HeraCeram: Rapid cooling
At the end of the programm the firing platform is completely and firing tray with objects is removed emediately. The firing tray can cool next to the furnace on a fire-resistant tray.
Others: Slow cooling
Depending on programming of the furnace either slow cooling to the initial temperature can be performed for approx. 4 – 6 minutes or a tempering phase of 3 – 5 minutes can be set at approx. 800 °C (high-melting alloys) resp. at approx. 700 °C (low-melting alloys).
Rapid cooling can always be performed for oxide and opaque firings.
Hardening When veneered with ceramics, these alloys do not require any additional hardening process to provide their maximum physical values.
Solder / Laser welding wire
Prior to Ceramic Firing
Solder Herador PF Lot
Working temperature °C: 1010 / Solder colour: yellow
After Ceramic Firing
Solder Herador/Maingold PF Lot solder 800
Flux** Working temperature* 800°C / Solder colour: yellow
Alloy also available as Laser welding wire
Ø 0.5 mm x 200 mm -
Ø 0.3 mm x 200 mm +